Neomould® 1982-W-1 is a low styrene emitting, highly filled preaccelerated unsaturated polyester resin based on DCPD and low profile additives, dissolved in styrene.
Neomould® 1982-W-1 has low reactivity and viscosity and shows zero shrinkage upon cure.
Description
Neomould® 1982-W-1 is a low styrene-emitting, highly filled, pre-accelerated unsaturated polyester resin based on DCPD and low-profile additives, dissolved in styrene. It has low reactivity and viscosity and shows zero shrinkage upon cure.
| Property | Range | Unit | TM |
| Appearance | Hazy | - | TM 2265 |
| Viscosity, 23℃ Z2, 2s-1 | 620-680 | mPa.s | TM 2313 |
| Viscosity, 23℃ Z2, 50s-1 | 590-630 | mPa.s | TM 2313 |
| Viscosity, 23℃ Z2, 250s-1 | 530-560 | mPa.s | TM 2313 |
| Solids content, IR | 68-71 | % | TM 2033 |
| Gel time(25-35 °C) | 38-42 | min | TM 2625 |
| Cure time 25℃ to peak | 46-56 | min | TM 2625 |
| Peak temperature | 110-120 | ℃ | TM 2625 |
Because of its fast curing characteristics, combined with low peak exotherm in thin layers and zero-shrinkage behavior, this resin is extremely suitable for mould making.
The resin was designed with easy processing in mind: fiber wet-out is quick, without drag on the roller, and its color makes it easy to spot air pockets during laminating. It exhibits tack-free cure without affecting secondary bonding, and its thixotropy ensures it will not slip or drain from vertical surfaces.
● Zero-shrinkage behavior
● Quick fiber wet-out, no drag on roller
● Color aids air-pocket detection during laminating
● Tack-free cure without affecting secondary bonding
● Thixotropic — will not slip or drain from vertical surfaces